ASTM A333 Standard Specifications For Seamless And Welded Steel Pipe For Low-Temperature Service
DIMENSION : ASTM A333 Grade 3&Grade 6 seamless pipe for Low-Temperature
Types |
Wall Thickness (mm) |
|||||||||||||||||||||||||||||||||
mm |
2 |
3 |
4 |
5 |
6 |
7 |
8 |
9 |
10 |
11 |
12 |
13 |
14 |
15 |
16 |
17 |
18 |
19 |
20 |
21 |
22 |
23 |
24 |
25 |
26 |
27 |
28 |
29 |
30 |
31 |
32 |
33 |
34 |
35 |
10.29 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
13.72 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
17.14 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
21.34 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
26.67 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
33.4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
42.16 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
48.26 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
60.32 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
73 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
76.1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
82.5 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
88.9 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
101.6 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
114.3 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
127 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
139.7 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
152.4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
159 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
168.3 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
177.8 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
193.7 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
203 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
219.1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
244.5 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
273 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
298.5 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
323.8 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
339.7 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
355.6 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
406.4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
457.2 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
473.1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
508 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
530 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
558.8 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
609.6 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
630 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Chemical Composition OF ASTM A333 Grade 3&Grade6 seamless pipe for Low-Temperature
Standard |
ASTM A333 |
||||||||||
Grades |
C |
Si |
Mn |
S |
P |
Cr |
Ni |
Mo |
Cu |
V |
Al |
16MnDG |
0.12-0.20 |
0.20-0.55 |
1.20-1.60 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
-- |
-- |
10MnDG |
≤0.13 |
0.17-0.37 |
≤1.35 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
≤0.07 |
-- |
09DG |
≤0.12 |
0.17-0.37 |
≤0.95 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
≤0.07 |
-- |
09Mn2VDG |
≤0.12 |
0.17-0.37 |
≤1.85 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
≤0.12 |
-- |
06Ni3MoDG |
≤0.08 |
0.17-0.37 |
≤0.85 |
≤0.025 |
≤0.025 |
-- |
2.5-3.7 |
0.15-0.30 |
-- |
≤0.05 |
-- |
A333Gr1 |
≤0.30 |
-- |
0.40-1.06 |
0≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
-- |
-- |
A333Gr3 |
≤0.19 |
0.18-0.37 |
0.31-0.64 |
≤0.025 |
≤0.025 |
-- |
3.18-3.82 |
-- |
-- |
-- |
-- |
A333Gr4 |
≤0.12 |
0.18-0.37 |
0.50-1.05 |
≤0.025 |
≤0.025 |
0.44-1.01 |
0.47-0.98 |
-- |
0.40-0.75 |
-- |
0.04-0.30 |
A333Gr6 |
≤0.30 |
≥0.10 |
0.29-1.06 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
-- |
-- |
A333Gr7 |
≤0.19 |
0.13-0.32 |
≤0.90 |
≤0.025 |
≤0.025 |
-- |
2.03-2.57 |
-- |
-- |
-- |
-- |
A333Gr8 |
≤0.13 |
0.13-0.32 |
≤0.90 |
≤0.025 |
≤0.025 |
-- |
8.40-9.60 |
-- |
-- |
-- |
-- |
A333Gr9 |
≤0.20 |
-- |
0.40-1.06 |
≤0.025 |
≤0.025 |
-- |
1.60-2.24 |
-- |
0.75-1.25 |
-- |
-- |
A333Gr10 |
≤0.20 |
0.10-0.35 |
1.15-1.50 |
≤0.015 |
≤0.030 |
≤0.15 |
≤0.25 |
≤0.50 |
≤0.015 |
≤0.12 |
≤0.06 |
A333Gr11 |
≤0.10 |
≤0.035 |
≤0.60 |
≤0.025 |
≤0.025 |
≤0.50 |
35.0-37.0 |
≤0.50 |
-- |
-- |
-- |
Mechanical Properties OFASTM A333 Grade 3& Grade 6 seamless pipe for Low-Temperature
Standard |
Grade |
Tensile Strength (MPa) |
Yield Point (MPa) |
Elongation (%) |
|
Y |
X |
||||
ASTM A333 |
Grade 1 |
≥ 380 |
≥ 205 |
≥ 35 |
≥ 25 |
Grade 3 |
≥ 450 |
≥ 240 |
≥ 30 |
≥ 20 |
|
Grade 4 |
≥ 415 |
≥ 240 |
≥ 30 |
≥ 16.5 |
|
Grade 6 |
≥ 415 |
≥ 240 |
≥ 30 |
≥ 16.5 |
|
Grade 7 |
≥ 450 |
≥ 240 |
≥ 30 |
≥ 22 |
|
Grade 8 |
≥ 690 |
≥ 515 |
≥ 22 |
|
|
Grade 9 |
≥ 435 |
≥ 315 |
≥ 28 |
|
|
Grade 10 |
≥ 550 |
≥ 450 |
≥ 22 |
|
|
Grade 11 |
≥ 450 |
≥ 240 |
≥ 18 |
|
Chemical Composition OF ASTM A333 Grade 3&Grade6 seamless pipe for Low-Temperature
Standard |
ASTM A333 |
||||||||||
Grades |
C |
Si |
Mn |
S |
P |
Cr |
Ni |
Mo |
Cu |
V |
Al |
16MnDG |
0.12-0.20 |
0.20-0.55 |
1.20-1.60 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
-- |
-- |
10MnDG |
≤0.13 |
0.17-0.37 |
≤1.35 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
≤0.07 |
-- |
09DG |
≤0.12 |
0.17-0.37 |
≤0.95 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
≤0.07 |
-- |
09Mn2VDG |
≤0.12 |
0.17-0.37 |
≤1.85 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
≤0.12 |
-- |
06Ni3MoDG |
≤0.08 |
0.17-0.37 |
≤0.85 |
≤0.025 |
≤0.025 |
-- |
2.5-3.7 |
0.15-0.30 |
-- |
≤0.05 |
-- |
A333Gr1 |
≤0.30 |
-- |
0.40-1.06 |
0≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
-- |
-- |
A333Gr3 |
≤0.19 |
0.18-0.37 |
0.31-0.64 |
≤0.025 |
≤0.025 |
-- |
3.18-3.82 |
-- |
-- |
-- |
-- |
A333Gr4 |
≤0.12 |
0.18-0.37 |
0.50-1.05 |
≤0.025 |
≤0.025 |
0.44-1.01 |
0.47-0.98 |
-- |
0.40-0.75 |
-- |
0.04-0.30 |
A333Gr6 |
≤0.30 |
≥0.10 |
0.29-1.06 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
-- |
-- |
A333Gr7 |
≤0.19 |
0.13-0.32 |
≤0.90 |
≤0.025 |
≤0.025 |
-- |
2.03-2.57 |
-- |
-- |
-- |
-- |
A333Gr8 |
≤0.13 |
0.13-0.32 |
≤0.90 |
≤0.025 |
≤0.025 |
-- |
8.40-9.60 |
-- |
-- |
-- |
-- |
A333Gr9 |
≤0.20 |
-- |
0.40-1.06 |
≤0.025 |
≤0.025 |
-- |
1.60-2.24 |
-- |
0.75-1.25 |
-- |
-- |
A333Gr10 |
≤0.20 |
0.10-0.35 |
1.15-1.50 |
≤0.015 |
≤0.030 |
≤0.15 |
≤0.25 |
≤0.50 |
≤0.015 |
≤0.12 |
≤0.06 |
A333Gr11 |
≤0.10 |
≤0.035 |
≤0.60 |
≤0.025 |
≤0.025 |
≤0.50 |
35.0-37.0 |
≤0.50 |
-- |
-- |
-- |
Mechanical Properties OFASTM A333 Grade 3& Grade 6 seamless pipe for Low-Temperature
Standard |
Grade |
Tensile Strength (MPa) |
Yield Point (MPa) |
Elongation (%) |
|
Y |
X |
||||
ASTM A333 |
Grade 1 |
≥ 380 |
≥ 205 |
≥ 35 |
≥ 25 |
Grade 3 |
≥ 450 |
≥ 240 |
≥ 30 |
≥ 20 |
|
Grade 4 |
≥ 415 |
≥ 240 |
≥ 30 |
≥ 16.5 |
|
Grade 6 |
≥ 415 |
≥ 240 |
≥ 30 |
≥ 16.5 |
|
Grade 7 |
≥ 450 |
≥ 240 |
≥ 30 |
≥ 22 |
|
Grade 8 |
≥ 690 |
≥ 515 |
≥ 22 |
|
|
Grade 9 |
≥ 435 |
≥ 315 |
≥ 28 |
|
|
Grade 10 |
≥ 550 |
≥ 450 |
≥ 22 |
|
|
Grade 11 |
≥ 450 |
≥ 240 |
≥ 18 |
|
DIMENSION : ASTM A333 Grade 3&Grade 6 seamless pipe for Low-Temperature
Types |
Wall Thickness (mm) |
|||||||||||||||||||||||||||||||||
mm |
2 |
3 |
4 |
5 |
6 |
7 |
8 |
9 |
10 |
11 |
12 |
13 |
14 |
15 |
16 |
17 |
18 |
19 |
20 |
21 |
22 |
23 |
24 |
25 |
26 |
27 |
28 |
29 |
30 |
31 |
32 |
33 |
34 |
35 |
10.29 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
13.72 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
17.14 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
21.34 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
26.67 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
33.4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
42.16 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
48.26 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
60.32 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
73 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
76.1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
82.5 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
88.9 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
101.6 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
114.3 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
127 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
139.7 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
152.4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
159 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
168.3 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
177.8 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
193.7 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
203 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
219.1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
244.5 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
273 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
298.5 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
323.8 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
339.7 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
355.6 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
406.4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
457.2 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
473.1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
508 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
530 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
558.8 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
609.6 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
630 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Chemical Composition OF ASTM A333 Grade 3&Grade6 seamless pipe for Low-Temperature
Standard |
ASTM A333 |
||||||||||
Grades |
C |
Si |
Mn |
S |
P |
Cr |
Ni |
Mo |
Cu |
V |
Al |
16MnDG |
0.12-0.20 |
0.20-0.55 |
1.20-1.60 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
-- |
-- |
10MnDG |
≤0.13 |
0.17-0.37 |
≤1.35 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
≤0.07 |
-- |
09DG |
≤0.12 |
0.17-0.37 |
≤0.95 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
≤0.07 |
-- |
09Mn2VDG |
≤0.12 |
0.17-0.37 |
≤1.85 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
≤0.12 |
-- |
06Ni3MoDG |
≤0.08 |
0.17-0.37 |
≤0.85 |
≤0.025 |
≤0.025 |
-- |
2.5-3.7 |
0.15-0.30 |
-- |
≤0.05 |
-- |
A333Gr1 |
≤0.30 |
-- |
0.40-1.06 |
0≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
-- |
-- |
A333Gr3 |
≤0.19 |
0.18-0.37 |
0.31-0.64 |
≤0.025 |
≤0.025 |
-- |
3.18-3.82 |
-- |
-- |
-- |
-- |
A333Gr4 |
≤0.12 |
0.18-0.37 |
0.50-1.05 |
≤0.025 |
≤0.025 |
0.44-1.01 |
0.47-0.98 |
-- |
0.40-0.75 |
-- |
0.04-0.30 |
A333Gr6 |
≤0.30 |
≥0.10 |
0.29-1.06 |
≤0.025 |
≤0.025 |
-- |
-- |
-- |
-- |
-- |
-- |
A333Gr7 |
≤0.19 |
0.13-0.32 |
≤0.90 |
≤0.025 |
≤0.025 |
-- |
2.03-2.57 |
-- |
-- |
-- |
-- |
A333Gr8 |
≤0.13 |
0.13-0.32 |
≤0.90 |
≤0.025 |
≤0.025 |
-- |
8.40-9.60 |
-- |
-- |
-- |
-- |
A333Gr9 |
≤0.20 |
-- |
0.40-1.06 |
≤0.025 |
≤0.025 |
-- |
1.60-2.24 |
-- |
0.75-1.25 |
-- |
-- |
A333Gr10 |
≤0.20 |
0.10-0.35 |
1.15-1.50 |
≤0.015 |
≤0.030 |
≤0.15 |
≤0.25 |
≤0.50 |
≤0.015 |
≤0.12 |
≤0.06 |
A333Gr11 |
≤0.10 |
≤0.035 |
≤0.60 |
≤0.025 |
≤0.025 |
≤0.50 |
35.0-37.0 |
≤0.50 |
-- |
-- |
-- |
Mechanical Properties OFASTM A333 Grade 3& Grade 6 seamless pipe for Low-Temperature
Standard |
Grade |
Tensile Strength (MPa) |
Yield Point (MPa) |
Elongation (%) |
|
Y |
X |
||||
ASTM A333 |
Grade 1 |
≥ 380 |
≥ 205 |
≥ 35 |
≥ 25 |
Grade 3 |
≥ 450 |
≥ 240 |
≥ 30 |
≥ 20 |
|
Grade 4 |
≥ 415 |
≥ 240 |
≥ 30 |
≥ 16.5 |
|
Grade 6 |
≥ 415 |
≥ 240 |
≥ 30 |
≥ 16.5 |
|
Grade 7 |
≥ 450 |
≥ 240 |
≥ 30 |
≥ 22 |
|
Grade 8 |
≥ 690 |
≥ 515 |
≥ 22 |
|
|
Grade 9 |
≥ 435 |
≥ 315 |
≥ 28 |
|
|
Grade 10 |
≥ 550 |
≥ 450 |
≥ 22 |
|
|
Grade 11 |
≥ 450 |
≥ 240 |
≥ 18 |
|
ASTM A333 Grade 3&Grade 6 seamless pipe for Low-Temperature Manufacturing Process :
tube perforation → → → heated three-roll cross-rolling, continuous rolled or extruded-cannula → sizing (or reducing) steel tube straightening → → → → cooling water pressure test (or testing) → tags → storage. Drawing (rolling) seamless steel pipe: pipe perforated → heat → → → → start → annealing pickling oil (copper) → multi-pass drawing (cold rolled) steel tube heat treatment straightening → → → → hydrostatic test (testing) → tags → storage.
There are probably hundreds of different methods for packing a pipe, and most of them have merit, but there are two principles that are vital for any method to work prevent rusting and Sea transportation security.
● Plastic caps plugged at the two sides of pipe ends
● Should be avoided by the steel strapping and transport damage
● Bundled signs should be uniform and consistent
● The same bundle(batch) of steel pipe should be came from the same furnace.
● The steel pipe has the same furnace number, the same steel grade, the same specifications.
Our packing can meet any needs of the customers